Evaluation of the Mechanical and Physical Properties of Portland Cement Mortar with the Addition of Rosin Resin in Confined Masonry Walls
Article Sidebar
Main Article Content
Abstract
This study is justified by the need to improve the moisture-resistant properties of Portland cement mortar, one of the main problems in buildings located in humid areas, affecting both the durability and habitability of homes. The objective was to evaluate the impact of adding rosin resin on the mechanical and physical properties of mortar used in confined masonry walls. The main objective was to determine whether this addition improves impermeability and adhesion without significantly compromising structural strength. To this end, tests were conducted in accordance with Peruvian and Chilean technical standards, including prism compression tests, diagonal compression tests on low walls, flexural strength, water absorption, and shear adhesion tests, using mortars with rosin percentages of 0.2%, 0.4%, and 0.5% at different dosages. The results showed that the addition of rosin reduces the mortar's compressive and flexural strength, as well as its stiffness. However, it significantly improves impermeability and adhesion, especially at dosages of 0.2% and 0.4% resin. It was concluded that although the use of rosin diminishes certain mechanical properties, its physical benefits, such as reduced capillary absorption and increased adhesion, make it a viable alternative in homes with up to two floors, in contexts where humidity control is a priority over structural strength.
Downloads
Metrics
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
References
D. Heras Murcia, Artist, Morteros de cemento con nano-adiciones de hierro y sílice [tesis de maestría, Universidad politécnica de Madrid]. [Art]. Repositorio digital, 2015.
J. Alcaide Romero, Artist, Caracterización de morteros con adición o sustitución de diferentes materiales carbonosos [Tesis de doctorado, Universidad de Alicante]. [Art]. Repositorio digital, 2007.
A. Adco Mamani y A. Apaza Mamani, Artists, Influencia del Polietileno en la Humedad por Capilaridad en Muros de Mampostería en la Urbanización Clara Victoria-Juliaca [Tesis para obtar al título de ingeniero civil]. [Art]. Universidad Cesar Vallejo, 2022.
J. P. Fernandez Curotto, Artist, Humedad proveniente del suelo en edificaciones [Tesis de titulación, Universidad nacional de chile]. [Art]. Repositorio digital, 2008.
N. Proietti, P. Calicchia, F. Colao, S. De Simone, V. Di Tullio, L. Luvidi, F. Prestileo, M. Romani y A. Tatì, «Moisture Damage in Ancient Masonry: A Multidisciplinary Approach for In Situ Diagnostics,» Minerals, vol. 11, nº 406, p. 23, 2021.
L. B. Pusaclla Bernal, Artist, Los suelos con alto contenido de sales influyen en los daños en viviendas autoconstruidas en la zona II de Tahuantinsuyo- Independencia 2017 [Tesis de titulación, Universidad César Vallejo]. [Art]. Repositorio digital, 2017.
INACAL, «Análisis granulométrico del agregado fino, grueso y global,» Lima, 2001.
INACAL, «Método de ensayo normalizado para la densidad, la densidad relativa (peso específico) y absorción del agregado fino,» Lima, 2013.
INACAL, «Método de ensayo normalizado para contenido de humedad total evaporable de agregados por secado,» Lima, 2013.
INACAL, «Método de ensayo normalizado para determinar la masa por unidad de volumen o densidad ("peso unitario") y los vacios en los agregados,» Lima, 2011.
INACAL, «Método de ensayo para la determinación de la resistencia en compresión de prismas de albailería,» Lima, 2013.
INACAL, «Método de ensayo de compresión diagonal en muretes de albañilería,» Lima, 2004.
R. Yaipen Trelles, Artist, Determinación del módulo de elasticidad, coeficiente de poisson, módulo de corte, del concreto, utilizando materiales de la región de Piura [tesis para optar al título, Universidad católica Santo Toribio de Mogrovejo]. [Art]. Repositorio digital, 2022.
A. San Bartolomé, D. Quiun y W. Silva, Diseño y construcción de estructuras sismoresistentes de albañilería, Lima: Fondo editorial Pontificia Universidad Católica del Perú, 2018.
C. R. Catalán Oliva, «Algunas consideraciones sobre el modulo de poisson,» Unidad de investigación y desarrollo vial, San salvador, 2008.
INACAL, «Método de ensayo normalizado de resistencia a la flexión de morteros de cemento portland,» Lima, 2002.
INACAL, «Método de ensayo normalizado para la tasa de absorción del agua de morteros de albañileria,» Lima, 2015.
INN, «Construcción-Ladrillos cerámicos-Ensayos,» Chile, 2001.
M. Fernandez Cánovas, N. Hurtado y G. Kawiche, «Influencia que sobre las propiedades físico-mecánicas de los morteros de cemento portland tiene la adición de colofonia y tanino,» Materiales de construcción, vol. 39, nº 216, pp. 15-22, 1989.
G. Sosa Davila, Artist, Efecto del biopolímero extraido de pinus radiata como aditivo en las propiedades del concreto Huancayo - Junin 2018. [Art]. Universidad Nacional de Centro del Peru, 2019.
O. Hernández y R. Meli, Artists, Modalidades de refuerzo para mejorar el comportamiento sísmico de muros de mampostería. [Art]. UNAM, 1976.